TestWorks Report file:///C:/DOCUME~1/Tom/USTAWI~1/Temp/TW4_Temp/htm1F4.html Próba statycznego rozciagania 2014-04-09

Materiał: stal 18G2A AGH, IMiR

Grupa:

Zmęczenie materiału pod kontrolš Operator: Tomasz Machniewicz Wyniki badania Name

Value

Units

BaseLength

50.00 mm

Diameter

9.980 mm

DiameterAfterFailure 5.230 mm

Measured Elongation 66.00 mm

Area

78.2 mm^2

Load At Offset Yield 34787 N

Stress At Offset Yield 444.70 MPa

Load At Yield

38675.9 N

Stress At Yield 494.41 MPa

Peak Load

45674 N

Ultimate Stress 583.88 MPa

Break Load

27823 N

Eng Break Stress 355.67 MPa

True Break Stress 613.67 MPa

Elongation to failure (A5) 32.00 %

Necking

72.54 %

Modulus

203752.7 MPa

PoissonRatio

0.306

StrainHardeningExponent (n) 0.058

StrainHardeningCooficient 647.9 MPa

(H)

1 z 2

2014-04-09 17:45

TestWorks Report file:///C:/DOCUME~1/Tom/USTAWI~1/Temp/TW4_Temp/htm1F4.html 2 z 2

2014-04-09 17:45