Próba statycznego rozciagania
Materiał: stal 18G2A

2014-04-09

AGH, IMiR

Grupa:

Zm

ę

czenie materiału pod kontrolš

Operator: Tomasz Machniewicz

Wyniki badania

Name

Value

Units

BaseLength

50.00 mm

Diameter

9.980 mm

DiameterAfterFailure

5.230 mm

Measured Elongation

66.00 mm

Area

78.2 mm^2

Load At Offset Yield

34787 N

Stress At Offset Yield

444.70 MPa

Load At Yield

38675.9 N

Stress At Yield

494.41 MPa

Peak Load

45674 N

Ultimate Stress

583.88 MPa

Break Load

27823 N

Eng Break Stress

355.67 MPa

True Break Stress

613.67 MPa

Elongation to failure (A5)

32.00 %

Necking

72.54 %

Modulus

203752.7 MPa

PoissonRatio

0.306

StrainHardeningExponent (n)

0.058

StrainHardeningCooficient
(H)

647.9 MPa

TestWorks Report

file:///C:/DOCUME~1/Tom/USTAWI~1/Temp/TW4_Temp/htm1F4.html

1 z 2

2014-04-09 17:45

TestWorks Report

file:///C:/DOCUME~1/Tom/USTAWI~1/Temp/TW4_Temp/htm1F4.html

2 z 2

2014-04-09 17:45