Materiał |
Oznaczenia wg PN |
HBnom daN/mm2 |
ko MPa |
Zo MPa |
staliwo |
39 L |
150 |
2,4 |
195 |
staliwo |
40 L |
175 |
3,4 |
225 |
stal |
St 4 |
125 |
2.8 |
210 |
stal |
St 5 |
150 |
4,0 |
250 |
stal |
St 6 |
180 |
4,8 |
275 |
stal |
St 8 |
210 |
8,0 |
300 |
stal ulepszona ciepl. |
25 |
140 |
2,6 |
250 |
stal ulepszona ciepl. |
45 |
185 |
4,5 |
300 |
stal ulepszona ciepl. |
65 |
210 |
5,7 |
330 |
stal ulepszona ciepl. |
35 H |
260 |
9,0 |
390 |
stal ulepszona ciepl. |
35 SG |
230 |
6,2 |
400 |
stal ulepszona ciepl. |
40 HM |
300 |
9,0 |
410 |
stal nawęglana |
10 |
636 |
55,0 |
290 |
stal nawęglana |
15 HGA |
650 |
56,0 |
550 |
stal nawęglana |
20 HGA |
650 |
56,0 |
610 |
stal nawęglana |
12 H2N4A |
650 |
56,0 |
570 |
stal nawęglana |
15 HN |
650 |
56,0 |
570 |
stal nawęglana |
18 H2N2 |
650 |
56,0 |
610 |
stal hartow. pow. |
45 |
595 |
48,0 |
410 |
stal hartow. pow. |
35 SG |
560 |
42,0 |
440 |
stal hartow. pow. |
40 H |
587 |
47,0 |
450 |
stal azotowana |
40 H |
' 595 |
48,0 |
420 |
stal azotowana |
35, SG |
550 |
40,0 |
450 |
Uwaga: W przypadku jednostronnego zginania zębów do obliczeń przyjmuje się Z. - Z0, w przypadku obustronnego zginania Z, = 0,75Z0. Dla tekstolitów przyjmuje się k0 = 2,0-r2,6 N/mm2 oraz Z0 = 70-*-80 N/mm1,