Metoda PO

ρ_pt = ............................. [kg/dm³] m = .........................[kg] V = ............................. [dm³]

ρ_prz = m/V [kg/dm³] = ......................................................................... [kg/dm³]

SZCZELNOŚĆ s = ρ_prz / ρ_pt s = ...............................

POROWATOŚĆ p = (1-s) 100 [%] p = ..................................................................%

ILOŚĆ POWIETRZA (w 1 dm³) P = ..................................................................

RZECZYWISTE ILOŚCI SKŁADNIKÓW MIESZANKI BETONOWEJ

C_rz = C × s = ..................................................................... [kg]

K_rz = K × s = ..................................................................... [kg]

W_rz = W × s = ..................................................................... [kg]

SPODZIEWANA WYTRZYMAŁOŚC ŚREDNIA

= ........................[MPa] f_ck = f_cm -6 = .................. [MPa]

KLASA BETONU: C......./........

UZYSKANA WYTRZYMAŁOŚĆ NA ŚCISKANIE

Przeliczenie wytrzymałości z kostek o boku 10cm na kostki o boku 15cm

[MPa] gdzie: ω = 0,90 A = ściskana pow. próbki w m²

F = największe obciążenie przeniesione przez próbkę w kN

Po ....... dniach:

F₁ = ............... [kN] → f_c1^... = ...................................................................................[MPa]

F₂ = ............... [kN] → f_c2^... = ...................................................................................[MPa]

F₃ = ............... [kN] → f_c3^...= ...................................................................................[MPa]

Wytrzymałość po ...... dniach stanowi ...... % wytrzymałości 28 - dniowej

f_c1²⁸ = ...................................................................................[MPa]

f_c2²⁸ = ...................................................................................[MPa]

f_c3²⁸ = ...................................................................................[MPa]

Wytrzymałość średnia f_cm = (f_c1²⁸ + f_c2²⁸ + f_c3²⁸ ) : 3 = ................................................[MPa]

Dla n = 3

• 
  (kryt.1)

• 
  (kryt.2)

UZYSKANA KLASA BETONU: C......./........

Po 28 dniach:

F₁ = ............... [kN] → f_c1²⁸ = ...................................................................................[MPa]

F₂ = ............... [kN] → f_c2²⁸ = ...................................................................................[MPa]

F₃ = ............... [kN] → f_c3²⁸ = ...................................................................................[MPa]

Wytrzymałość średnia f_cm = (f_c1²⁸ + f_c2²⁸ + f_c3²⁸ ) : 3 = ................................................[MPa]

Dla n = 3

• 
  (kryt.1)

• 
  (kryt.2)

UZYSKANA KLASA BETONU: C......./........

Metoda 3R

ρ_pt = ............................. [kg/dm³] m = .........................[kg] V = ............................. [dm³]

ρ_prz = m/V [kg/dm³] = ......................................................................... [kg/dm³]

SZCZELNOŚĆ s = ρ_prz / ρ_pt s = ...............................

POROWATOŚĆ p = (1-s) 100 [%] p = ..................................................................%

ILOŚĆ POWIETRZA (w 1000 dm³) P = ..................................................................

RZECZYWISTE ILOŚCI SKŁADNIKÓW MIESZANKI BETONOWEJ

C_rz = C × s = ..................................................................... [kg]

K_rz = K × s = ..................................................................... [kg]

W_rz = W × s = ..................................................................... [kg]

SPODZIEWANA WYTRZYMAŁOŚC ŚREDNIA

= ........................[MPa] f_ck = f_cm -6 = .................. [MPa]

KLASA BETONU: C......./........

UZYSKANA WYTRZYMAŁOŚĆ NA ŚCISKANIE

Przeliczenie wytrzymałości z kostek o boku 10cm na kostki o boku 15cm

[MPa] gdzie: ω = 0,90 A = ściskana pow. próbki w m²

F = największe obciążenie przeniesione przez próbkę w kN

Po ..... dniach:

F₁ = ............... [kN] → f_c1^... = ...................................................................................[MPa]

F₂ = ............... [kN] → f_c2^... = ...................................................................................[MPa]

F₃ = ............... [kN] → f_c3^... = ...................................................................................[MPa]

Wytrzymałość po ...... dniach stanowi ....... % wytrzymałości 28 - dniowej

f_c1²⁸ = ...................................................................................[MPa]

f_c2²⁸ = ...................................................................................[MPa]

f_c3²⁸ = ...................................................................................[MPa]

Wytrzymałość średnia f_cm = (f_c1²⁸ + f_c2²⁸ + f_c3²⁸ ) : 3 = ................................................[MPa]

Dla n = 3

• 
  (kryt.1)

• 
  (kryt.2)

UZYSKANA KLASA BETONU: C......./........

Politechnika Gdańska Laboratorium z Technologii Betonu

Katedra Konstrukcji Betonowych i Technologii Betonu WILiŚ, rok II, semestr 4

Lucyna Grabarczyk 1

---